ASME SA-29/SA-29M Grade 47L18 Introduce
ASME SA-29/SA-29M Grade 47L18 steel has several advantageous properties that make it suitable for various applications. It is strong, yet ductile and malleable, making it suitable for a variety of parts needing to handle high pressure or vibration. Additionally, it offers excellent resistance to both corrosion and wear, making it suitable for outdoor applications.
Smelting temperature:1589°C - 1364°C
Application:General requirements for hot working and cold finishing carbon steel and alloy steel bars
ASME SA-29/SA-29M Grade 47L18 Material Chemical Composition
The chemical composition of the ASME SA-29/SA-29M Grade 47L18 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Silicon (Si) | 0.1500 | 0.3500 |
| Sulfur (S) | - | 0.0400 |
| Lead (Pb) | 0.1500 | 0.3500 |
| PhOsphorus (P) | - | 0.0350 |
| Nickel (Ni) | 0.9000 | 1.2000 |
| Molybdenum (Mo) | 0.3000 | 0.4000 |
| Manganese (Mn) | 0.7000 | 0.9000 |
| Copper (Cu) | - | 0.3500 |
| Chromium (Cr) | 0.3500 | 0.5500 |
| Carbon (C) | 0.1600 | 0.2100 |
ASME SA-29/SA-29M Grade 47L18 Material Mechanical Properties
ASME SA-29/SA-29M Grade 47L18 steel has many desirable mechanical properties, including high strength, good ductility, and excellent impact resistance. The tensile strength of ASME SA-29/SA-29M Grade 47L18 steel is specified as a minimum of 85,000 psi. This is considered a high strength steel, making it a great choice for applications that require parts that are strong and can withstand high levels of stress.
The mechanical properties of the ASME SA-29/SA-29M Grade 47L18 steel are as follows:
| YieldRp0.2 | ≤ 898 (MPa) |
| TeileRm | ≤ 391 (MPa) |
| ImpactKV/Ku | 43(J) |
| ElongationA | 41% |
| Reduction in cross section on fractureZ | 24% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 344 |
ASME SA-29/SA-29M Grade 47L18 Material Thermal Properties
The thermal performance parameters of the ASME SA-29/SA-29M Grade 47L18 steel are as follows:
| Temperature (°C) | 32 | 451 | 498 |
| Modulus of elasticity (GPa) | - | 974 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 41 |
| Thermal conductivity (W/m·°C) | - | 23.3 | 12.2 |
| Specific thermal capacity (J/kg·°C) | - | 433 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.23 | - | - |
| Deity (kg/dm³) | - | - | 422 |
| Poisson’s coefficient, ν | - | - | 231 |
ASME SA-29/SA-29M Grade 47L18 Material Machining Technology
ASME SA-29/SA-29M Grade 47L18 steel is a high-strength, low-alloy steel carburized. It is one of the primary choices when it comes to carburizing steel. The material is composed of a combination of iron, chromium, vanadium, and molybdenum. It is also a low-cost and easily worked material, making it an ideal choice for a variety of applications.