EN 10088-1 X2NiCrAlTi32-20 Introduce
The mechanical properties of EN 10088-1 X2NiCrAlTi32-20 steel include tensile strength, yield strength, creep strength, fatigue strength, modulus of elasticity, hardness and impact strength. These are all important factors to consider when designing and building structures that require steel components, as these mechanical properties define how a particular steel will perform in different situations.
Smelting temperature:1887°C - 1114°C
Application:Stainless steels. List of stainless steels
EN 10088-1 X2NiCrAlTi32-20 Material Chemical Composition
The chemical composition of the EN 10088-1 X2NiCrAlTi32-20 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Carbon (C) | - | 0.0300 |
| Manganese (Mn) | - | 1.0000 |
| PhOsphorus (P) | - | 0.0200 |
| Sulfur (S) | - | 0.0150 |
| Silicon (Si) | - | 0.7000 |
| Nickel (Ni) | 32.0000 | 35.0000 |
| Chromium (Cr) | 20.0000 | 23.0000 |
| Titanium (Ti) | - | 0.6000 |
| Aluminum (Al) | 0.1500 | 0.4500 |
| Titanium (Ti) | - | 0.6000 |
| Titanium (Ti) | - | 0.6000 |
EN 10088-1 X2NiCrAlTi32-20 Material Mechanical Properties
EN 10088-1 X2NiCrAlTi32-20 steels are also highly heat resistant. This property is the result of the combination of elements in the alloy, as well as the specific heat treatments used in the fabrication of the steel. This property makes EN 10088-1 X2NiCrAlTi32-20 steels a great choice for applications where the steel must be subjected to high temperatures, such as components of a vehicle's exhaust system.
The mechanical properties of the EN 10088-1 X2NiCrAlTi32-20 steel are as follows:
| YieldRp0.2 | ≤ 595 (MPa) |
| TeileRm | ≤ 159 (MPa) |
| ImpactKV/Ku | 44(J) |
| ElongationA | 22% |
| Reduction in cross section on fractureZ | 13% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 412 |
EN 10088-1 X2NiCrAlTi32-20 Material Thermal Properties
The thermal performance parameters of the EN 10088-1 X2NiCrAlTi32-20 steel are as follows:
| Temperature (°C) | 41 | 565 | 569 |
| Modulus of elasticity (GPa) | - | 336 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 23 |
| Thermal conductivity (W/m·°C) | - | 44.3 | 32.2 |
| Specific thermal capacity (J/kg·°C) | - | 334 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.31 | - | - |
| Deity (kg/dm³) | - | - | 213 |
| Poisson’s coefficient, ν | - | - | 243 |
EN 10088-1 X2NiCrAlTi32-20 Material Machining Technology
Steel is one of the most commonly used metal alloys in the world. It is known for its strength, durability, and resistance to corrosion, among other properties. EN 10088-1 is an internationally accepted standard for steel sheet and plate products, and it is one of the most popular grades of stainless steel used in the manufacture of machine parts and components. In order to obtain the desired shape and size, machining must be done to EN 10088-1 X2NiCrAlTi32-20 steel.