ASTM A600 T11336 Introduce
ASTM A600 T11336 steel is a type of high strength, alloyed steel that has been used for various engineering and industrial applications since the mid 20th century. It is a versatile material that is both light and strong, while steel with this name may often be referred to as a "general purpose steel" because of its wide range of uses, ASTM A600 T11336 steel is actually a specific grade of steel, with specific chemical properties and specifications.
Smelting temperature:1854°C - 1437°C
Application:Tool Steel High Speed
ASTM A600 T11336 Material Chemical Composition
The chemical composition of the ASTM A600 T11336 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Tungsten (W) | 5.5000 | 6.5000 |
| Vanadium (V) | 1.7500 | 2.2500 |
| Silicon (Si) | 0.2000 | 0.4500 |
| Sulfur (S) | - | 0.0300 |
| PhOsphorus (P) | - | 0.0300 |
| (Ni+Cu) | - | 0.7500 |
| Molybdenum (Mo) | 4.5000 | 5.5000 |
| Manganese (Mn) | 0.1500 | 0.4000 |
| Chromium (Cr) | 3.7500 | 4.5000 |
| Cobalt (Co) | 7.7500 | 8.7500 |
| Carbon (C) | 0.8000 | 0.9000 |
ASTM A600 T11336 Material Mechanical Properties
The mechanical properties of the ASTM A600 T11336 steel are as follows:
| YieldRp0.2 | ≤ 686 (MPa) |
| TeileRm | ≤ 123 (MPa) |
| ImpactKV/Ku | 22(J) |
| ElongationA | 42% |
| Reduction in cross section on fractureZ | 24% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 111 |
ASTM A600 T11336 Material Thermal Properties
The thermal performance parameters of the ASTM A600 T11336 steel are as follows:
| Temperature (°C) | 12 | 253 | 363 |
| Modulus of elasticity (GPa) | - | 797 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 22 |
| Thermal conductivity (W/m·°C) | - | 24.3 | 41.2 |
| Specific thermal capacity (J/kg·°C) | - | 323 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.23 | - | - |
| Deity (kg/dm³) | - | - | 234 |
| Poisson’s coefficient, ν | - | - | 441 |