ASTM A29/A29M A29 15L26

ASTM A29/A29M A29 15L26 Steel,

ASTM A29/A29M A29 15L26

ASTM A29/A29M A29 15L26 is widely used in a variety of industries, including automotive, marine, construction, and general engineering applications. The ASTM A29/A29M A29 15L26 material standard is split into three broad categories, according to the tensile strength of the steel with which it is used. It is important to consult the relevant material standard prior to using ASTM A29/A29M A29 15L26 materials in order to ensure safe and appropriate usage.

If you need help, please contact us through the contact information below.

info@supplysteels.com

Contact us on WhatsApp

Call: 0086-371-86151827

ASTM A29/A29M A29 15L26 Introduce

ASTM A29/A29M A29 15L26 steel is a popular material choice among machine manufacturers due to its relative strength and ductility. It is an alloy of carbon and iron, and it has been used in machinery such as transmissions, gears, and bearings for many years. As with all metals, the mechanical properties of ASTM A29/A29M A29 15L26 steel depend on various factors, including composition, heat treatment, and other environmental conditions.

Smelting temperature:1152°C - 1932°C

Application:Hot forged and cold worked carbon steel and alloy steel rods

ASTM A29/A29M A29 15L26 Material Mechanical Properties

ASTM A29/A29M A29 15L26 steel also has good corrosion resistance. This corrosion resistance is due to the alloy's chromium content, which helps to form a thin protective layer on the steel's surface. This layer helps to prevent corrosion and can increase the life of the steel.

The mechanical properties of the ASTM A29/A29M A29 15L26 steel are as follows:

YieldRp0.2 ≤ 693 (MPa)
TeileRm≤ 473 (MPa)
ImpactKV/Ku43(J)
ElongationA34%
Reduction in cross section on fractureZ43%
As-Heat-Treated ConditionSolution and Aging, Annealing, Ausaging, Q+T,etc
Brinell hardness (HBW)212

ASTM A29/A29M A29 15L26 Material Thermal Properties

The thermal performance parameters of the ASTM A29/A29M A29 15L26 steel are as follows:

Temperature (°C)23891485
Modulus of elasticity (GPa)-223-
Mean coefficient of thermal expaion ×10-6/(°C)--22
Thermal conductivity (W/m·°C)-23.333.2
Specific thermal capacity (J/kg·°C)-421-
Specific electrical resistivity (Ω mm²/m)0.23--
Deity (kg/dm³)--444
Poisson’s coefficient, ν--113

ASTM A29/A29M A29 15L26 Material Machining Technology

When machining ASTM A29/A29M A29 15L26 steel, it is important to select the correct tooling for the job. High speed steel (HSS) and cobalt steel tools are the most commonly used for these materials. HSS tools that have been coated with titanium aluminum nitride (TiAlN) offer the best combination of cutting performance and tool wear resistance. For some operations, special-purpose cutting tools may be necessary in order to obtain the desired machining performance.