ASTM A686 Type W1-8 Grade C Introduce
ASTM A686 Type W1-8 Grade C is an iron-based chemical composition alloy steel developed to meet American Society for Testing and Materials requirements. It is a versatile steel that is available in a variety of forms and steels, and is widely used in the manufacturing of a variety of products, including bridges, automobiles, piping and other industrial products. It is composed primarily of iron, with a small amount of carbon, manganese, phosphorus and sulfur. The alloying elements of this steel are chromium, molybdenum, cobalt and vanadium, resulting in a durable steel that can be heat treated for a variety of purposes.This steel has excellent resistance to corrosion and wear, making it an ideal choice for a variety of applications. It is also resistant to fatigue, making it suitable for heavy loads and high stress levels.
Smelting temperature:1591°C - 1583°C
Application:Carbon tool steel
ASTM A686 Type W1-8 Grade C Material Chemical Composition
The chemical composition of the ASTM A686 Type W1-8 Grade C steel are as follows:
| Element | Min | Max |
|---|---|---|
| Tungsten (W) | - | 0.1500 |
| Vanadium (V) | 0.1500 | 0.3500 |
| Silicon (Si) | 0.1000 | 0.4000 |
| Sulfur (S) | - | 0.0300 |
| PhOsphorus (P) | - | 0.0300 |
| Nickel (Ni) | - | 0.2000 |
| Molybdenum (Mo) | - | 0.1000 |
| Manganese (Mn) | 0.1000 | 0.4000 |
| Copper (Cu) | - | 0.2000 |
| Chromium (Cr) | - | 0.3000 |
| Carbon (C) | 0.8000 | 0.9000 |
ASTM A686 Type W1-8 Grade C Material Mechanical Properties
The mechanical properties of the ASTM A686 Type W1-8 Grade C steel are as follows:
| YieldRp0.2 | ≤ 838 (MPa) |
| TeileRm | ≤ 241 (MPa) |
| ImpactKV/Ku | 33(J) |
| ElongationA | 32% |
| Reduction in cross section on fractureZ | 11% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 323 |
ASTM A686 Type W1-8 Grade C Material Thermal Properties
The thermal performance parameters of the ASTM A686 Type W1-8 Grade C steel are as follows:
| Temperature (°C) | 21 | 797 | 639 |
| Modulus of elasticity (GPa) | - | 173 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 43 |
| Thermal conductivity (W/m·°C) | - | 42.3 | 22.2 |
| Specific thermal capacity (J/kg·°C) | - | 431 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.24 | - | - |
| Deity (kg/dm³) | - | - | 411 |
| Poisson’s coefficient, ν | - | - | 111 |