ASTM A249/A249M Grade S20153 Introduce
ASTM A249/A249M Grade S20153 steel is an austenitic stainless steel specifically designed for use in boiler, superheater, and heat exchanger tubes. Its high chromium and nickel content make it highly resistant to corrosion and oxidation, and its high strength-to-weight ratio makes it suitable for a range of applications. Furthermore, the steel offers improved heat resistance and good weldability, making it ideal for operations involving higher temperatures.
Smelting temperature:1894°C - 1916°C
Application:Welded austenitic steel tubes for boilers, superheaters, heat exchangers and condensers
ASTM A249/A249M Grade S20153 Material Chemical Composition
The chemical composition of the ASTM A249/A249M Grade S20153 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Silicon (Si) | - | 0.7500 |
| Sulfur (S) | - | 0.0150 |
| PhOsphorus (P) | - | 0.0450 |
| Nickel (Ni) | 4.0000 | 5.0000 |
| Nitrogen (N) | 0.1000 | 0.2500 |
| Manganese (Mn) | 6.4000 | 7.5000 |
| Copper (Cu) | - | 1.0000 |
| Chromium (Cr) | 16.0000 | 17.5000 |
| Carbon (C) | - | 0.0300 |
ASTM A249/A249M Grade S20153 Material Mechanical Properties
Corrosion resistance is a measure of how resistant a material is to corrosion or rusting. ASTM A249/A249M Grade S20153 steel has excellent resistance to corrosion and can withstand exposure to most chemicals, such as acids, alkalis, and other corrosive substances.
The mechanical properties of the ASTM A249/A249M Grade S20153 steel are as follows:
| YieldRp0.2 | ≤ 385 (MPa) |
| TeileRm | ≤ 175 (MPa) |
| ImpactKV/Ku | 32(J) |
| ElongationA | 41% |
| Reduction in cross section on fractureZ | 12% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 311 |
ASTM A249/A249M Grade S20153 Material Thermal Properties
The thermal performance parameters of the ASTM A249/A249M Grade S20153 steel are as follows:
| Temperature (°C) | 32 | 655 | 758 |
| Modulus of elasticity (GPa) | - | 719 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 42 |
| Thermal conductivity (W/m·°C) | - | 33.3 | 33.2 |
| Specific thermal capacity (J/kg·°C) | - | 321 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.34 | - | - |
| Deity (kg/dm³) | - | - | 331 |
| Poisson’s coefficient, ν | - | - | 144 |
ASTM A249/A249M Grade S20153 Material Machining Technology
When it comes to machining ASTM A249/A249M Grade S20153 steel, there are several guidelines that should be followed to ensure optimal results. First and foremost, the cutting tool material should be of a high grade. ASTM A249/A249M Grade S20153 steel is extremely hard and can cause excessive wear and tear on lower-grade cutting tools. Second, the cutting speed should be carefully chosen. High cutting speeds can be used to reduce forces during machining; however, they can also reduce tool life. Therefore, it is essential to find the correct balance between cutting speed and tool life. Third, heavy-duty cutting fluids should be used during the machining process to ensure optimal results. The fluids should be capable of lubricating the material and preventing build-up of heat, which can cause the tool to lose its edge quickly.