ASME SA-29/SA-29M 10L49 Introduce
ASME SA-29/SA-29M 10L49 is an excellent carbon steel grade, with some of the best thermal properties in its class. It is particularly suitable for use in high-temperature applications, as it is able to resist temperatures up to 900°C and also has excellent thermal conductivity and expansion properties. As such, it is widely used in the aerospace, automotive and piping industries.
Smelting temperature:1536°C - 1343°C
Application:General requirements for hot working and cold finishing carbon steel and alloy steel bars
ASME SA-29/SA-29M 10L49 Material Chemical Composition
The chemical composition of the ASME SA-29/SA-29M 10L49 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Sulfur (S) | - | 0.0500 |
| Lead (Pb) | 0.1500 | 0.3500 |
| PhOsphorus (P) | - | 0.0400 |
| Manganese (Mn) | 0.6000 | 0.9000 |
| Copper (Cu) | 0.2000 | - |
| Carbon (C) | 0.4600 | 0.5300 |
| Boron (B) | 0.0005 | 0.0030 |
ASME SA-29/SA-29M 10L49 Material Mechanical Properties
ASME SA-29/SA-29M 10L49 steel has many desirable mechanical properties, including high strength, good ductility, and excellent impact resistance. The tensile strength of ASME SA-29/SA-29M 10L49 steel is specified as a minimum of 85,000 psi. This is considered a high strength steel, making it a great choice for applications that require parts that are strong and can withstand high levels of stress.
The mechanical properties of the ASME SA-29/SA-29M 10L49 steel are as follows:
| YieldRp0.2 | ≤ 183 (MPa) |
| TeileRm | ≤ 592 (MPa) |
| ImpactKV/Ku | 34(J) |
| ElongationA | 42% |
| Reduction in cross section on fractureZ | 13% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 214 |
ASME SA-29/SA-29M 10L49 Material Thermal Properties
The thermal performance parameters of the ASME SA-29/SA-29M 10L49 steel are as follows:
| Temperature (°C) | 32 | 718 | 152 |
| Modulus of elasticity (GPa) | - | 626 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 41 |
| Thermal conductivity (W/m·°C) | - | 11.3 | 44.2 |
| Specific thermal capacity (J/kg·°C) | - | 434 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.24 | - | - |
| Deity (kg/dm³) | - | - | 324 |
| Poisson’s coefficient, ν | - | - | 334 |
ASME SA-29/SA-29M 10L49 Material Machining Technology
ASME SA-29/SA-29M 10L49 steel is a high-strength, low-alloy steel carburized. It is one of the primary choices when it comes to carburizing steel. The material is composed of a combination of iron, chromium, vanadium, and molybdenum. It is also a low-cost and easily worked material, making it an ideal choice for a variety of applications.