ASME SA-29/SA-29M Grade 86L20 Introduce
ASME SA-29/SA-29M Grade 86L20 is an excellent choice for many different types of applications due to its combination of strength, formability, and weldability. It is a good choice for automotive components, tool steel, and structural steel. It is also a good option for applications where the material is subject to high levels of stress and strain. Overall, it is a great choice due to its cost and availability.
Smelting temperature:1975°C - 1533°C
Application:General requirements for hot working and cold finishing carbon steel and alloy steel bars
ASME SA-29/SA-29M Grade 86L20 Material Chemical Composition
The chemical composition of the ASME SA-29/SA-29M Grade 86L20 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Silicon (Si) | 0.1500 | 0.3500 |
| Sulfur (S) | - | 0.0400 |
| Lead (Pb) | 0.1500 | 0.3500 |
| PhOsphorus (P) | - | 0.0350 |
| Nickel (Ni) | 0.4000 | 0.7000 |
| Molybdenum (Mo) | 0.1500 | 0.2500 |
| Manganese (Mn) | 0.7000 | 0.9000 |
| Copper (Cu) | - | 0.3500 |
| Chromium (Cr) | 0.4000 | 0.6000 |
| Carbon (C) | 0.1800 | 0.2300 |
ASME SA-29/SA-29M Grade 86L20 Material Mechanical Properties
ASME SA-29/SA-29M Grade 86L20 steel has many desirable mechanical properties, including high strength, good ductility, and excellent impact resistance. The tensile strength of ASME SA-29/SA-29M Grade 86L20 steel is specified as a minimum of 85,000 psi. This is considered a high strength steel, making it a great choice for applications that require parts that are strong and can withstand high levels of stress.
The mechanical properties of the ASME SA-29/SA-29M Grade 86L20 steel are as follows:
| YieldRp0.2 | ≤ 995 (MPa) |
| TeileRm | ≤ 972 (MPa) |
| ImpactKV/Ku | 44(J) |
| ElongationA | 14% |
| Reduction in cross section on fractureZ | 21% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 342 |
ASME SA-29/SA-29M Grade 86L20 Material Thermal Properties
The thermal performance parameters of the ASME SA-29/SA-29M Grade 86L20 steel are as follows:
| Temperature (°C) | 22 | 555 | 478 |
| Modulus of elasticity (GPa) | - | 225 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 41 |
| Thermal conductivity (W/m·°C) | - | 12.3 | 21.2 |
| Specific thermal capacity (J/kg·°C) | - | 321 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.32 | - | - |
| Deity (kg/dm³) | - | - | 112 |
| Poisson’s coefficient, ν | - | - | 444 |
ASME SA-29/SA-29M Grade 86L20 Material Machining Technology
ASME SA-29/SA-29M Grade 86L20 steel is a high-strength, low-alloy steel carburized. It is one of the primary choices when it comes to carburizing steel. The material is composed of a combination of iron, chromium, vanadium, and molybdenum. It is also a low-cost and easily worked material, making it an ideal choice for a variety of applications.