ASME SA-29/SA-29M 1086 Introduce
The ASME SA-29/SA-29M 1086 specification is widely used and accepted in the industry. It is also accepted by many government and private organizations. The specification covers a wide range of bars and is suitable for many applications. It is commonly used in the fabrication of pressure vessels and other components that require hot-rolled carbon steel bars.
Smelting temperature:1674°C - 1472°C
Application:General requirements for hot working and cold finishing carbon steel and alloy steel bars
ASME SA-29/SA-29M 1086 Material Chemical Composition
The chemical composition of the ASME SA-29/SA-29M 1086 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Sulfur (S) | - | 0.0500 |
| PhOsphorus (P) | - | 0.0400 |
| Manganese (Mn) | 0.3000 | 0.5000 |
| Copper (Cu) | 0.2000 | - |
| Carbon (C) | 0.8000 | 0.9300 |
| Boron (B) | 0.0005 | 0.0030 |
ASME SA-29/SA-29M 1086 Material Mechanical Properties
ASME SA-29/SA-29M 1086 steel has many desirable mechanical properties, including high strength, good ductility, and excellent impact resistance. The tensile strength of ASME SA-29/SA-29M 1086 steel is specified as a minimum of 85,000 psi. This is considered a high strength steel, making it a great choice for applications that require parts that are strong and can withstand high levels of stress.
The mechanical properties of the ASME SA-29/SA-29M 1086 steel are as follows:
| YieldRp0.2 | ≤ 686 (MPa) |
| TeileRm | ≤ 986 (MPa) |
| ImpactKV/Ku | 41(J) |
| ElongationA | 12% |
| Reduction in cross section on fractureZ | 23% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 331 |
ASME SA-29/SA-29M 1086 Material Thermal Properties
The thermal performance parameters of the ASME SA-29/SA-29M 1086 steel are as follows:
| Temperature (°C) | 44 | 838 | 957 |
| Modulus of elasticity (GPa) | - | 734 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 33 |
| Thermal conductivity (W/m·°C) | - | 33.3 | 14.2 |
| Specific thermal capacity (J/kg·°C) | - | 341 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.31 | - | - |
| Deity (kg/dm³) | - | - | 423 |
| Poisson’s coefficient, ν | - | - | 442 |
ASME SA-29/SA-29M 1086 Material Machining Technology
ASME SA-29/SA-29M 1086 steel is a high-strength, low-alloy steel carburized. It is one of the primary choices when it comes to carburizing steel. The material is composed of a combination of iron, chromium, vanadium, and molybdenum. It is also a low-cost and easily worked material, making it an ideal choice for a variety of applications.