EN 10083-3 1.6510 Introduce
EN 10083-3 1.6510 steel is often used for a variety of applications. It is widely used in the automotive industry for components such as pistons, crankshafts, and connecting rods. In the aerospace industry, the steel is often used for components such as turbine blades and air frame components.
Smelting temperature:1766°C - 1246°C
Application:Steels for quenching and tempering - part 3: technical delivery conditions for alloy steels
EN 10083-3 1.6510 Material Chemical Composition
The chemical composition of the EN 10083-3 1.6510 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Silicon (Si) | - | 0.4000 |
| Sulfur (S) | - | 0.0350 |
| PhOsphorus (P) | - | 0.0250 |
| Nickel (Ni) | 0.7000 | 1.0000 |
| Molybdenum (Mo) | 0.1500 | 0.2500 |
| Manganese (Mn) | 0.5000 | 0.8000 |
| Chromium (Cr) | 0.6000 | 1.0000 |
| Carbon (C) | 0.3500 | 0.4300 |
EN 10083-3 1.6510 Material Mechanical Properties
The EN 10083-3 steels standard also contains requirements for the mechanical properties of steel products, including minimum values for tensile strength, yield strength, elongation, impact energy and hardness. These requirements vary depending on the grade of the steel product, with higher grades requiring higher mechanical property values.
The mechanical properties of the EN 10083-3 1.6510 steel are as follows:
| YieldRp0.2 | ≤ 658 (MPa) |
| TeileRm | ≤ 783 (MPa) |
| ImpactKV/Ku | 31(J) |
| ElongationA | 41% |
| Reduction in cross section on fractureZ | 14% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 113 |
EN 10083-3 1.6510 Material Thermal Properties
The thermal performance parameters of the EN 10083-3 1.6510 steel are as follows:
| Temperature (°C) | 12 | 178 | 715 |
| Modulus of elasticity (GPa) | - | 931 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 42 |
| Thermal conductivity (W/m·°C) | - | 34.3 | 12.2 |
| Specific thermal capacity (J/kg·°C) | - | 431 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.41 | - | - |
| Deity (kg/dm³) | - | - | 342 |
| Poisson’s coefficient, ν | - | - | 123 |
EN 10083-3 1.6510 Material Machining Technology
EN 10083-3 is a standard for the manufacture of heat-treatable steels. It is widely used in the automotive, construction and agricultural industries as well as other sectors. It offers a high level of strength and wear resistance with a good level of mechanical properties. Standard EN 10083-3 outlines the requirements for the machining of this steel, including its optimum machining parameters, cutting tools and speeds, workpiece setup and coolant selection.