SAE J438 W209 Introduce
SAE J438 W209 is a type of steel that is used in a variety of applications ranging from automotive to industrial parts and frames. With its good strength-to-weight ratio and weldability, it is an economical alternative to more expensive steels. The mechanical properties of SAE J438 W209 include tensile strength and yield strength. Tensile strength is the measure of how well the steel resisted being pulled apart when tension was applied. Yield strength is the measure of how well the steel resisted permanent deformation when it was subject to external forces.
Smelting temperature:1935°C - 1819°C
Application:Tool and die steels
SAE J438 W209 Material Chemical Composition
The chemical composition of the SAE J438 W209 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Vanadium (V) | 0.1500 | 0.3500 |
| Silicon (Si) | - | 0.3500 |
| (Mn+Si+Cr) | - | 0.7500 |
| Manganese (Mn) | - | 0.3500 |
| Chromium (Cr) | - | 0.1500 |
| Carbon (C) | 0.8500 | 0.9500 |
SAE J438 W209 Material Mechanical Properties
The mechanical properties of the SAE J438 W209 steel are as follows:
| YieldRp0.2 | ≤ 534 (MPa) |
| TeileRm | ≤ 124 (MPa) |
| ImpactKV/Ku | 12(J) |
| ElongationA | 21% |
| Reduction in cross section on fractureZ | 42% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 112 |
SAE J438 W209 Material Thermal Properties
The thermal performance parameters of the SAE J438 W209 steel are as follows:
| Temperature (°C) | 41 | 776 | 647 |
| Modulus of elasticity (GPa) | - | 195 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 43 |
| Thermal conductivity (W/m·°C) | - | 21.3 | 23.2 |
| Specific thermal capacity (J/kg·°C) | - | 214 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.41 | - | - |
| Deity (kg/dm³) | - | - | 422 |
| Poisson’s coefficient, ν | - | - | 413 |