JIS G3114 SMA570W Introduce
Steel as a material can be roughly divided into two major types, ferrous and non-ferrous. Ferrous materials include steel, iron, and alloys. The JIS G3114 SMA570W mainly defines the requirements for steel plates, but it also covers other steel products, including cold-rolled steel returns, structural steel, welded wire mesh and universal plates.
Smelting temperature:1797°C - 1198°C
Application:Hot rolled atmospheric corrosion resistant welded structural steel
JIS G3114 SMA570W Material Chemical Composition
The chemical composition of the JIS G3114 SMA570W steel are as follows:
| Element | Min | Max |
|---|---|---|
| Silicon (Si) | 0.1500 | 0.6500 |
| Sulfur (S) | - | 0.0350 |
| PhOsphorus (P) | - | 0.0350 |
| Nickel (Ni) | 0.0500 | 0.3000 |
| Manganese (Mn) | - | 1.4000 |
| Copper (Cu) | 0.3000 | 0.5000 |
| Chromium (Cr) | 0.4500 | 0.7500 |
| (CEV) | - | 0.4400 |
| Carbon (C) | - | 0.1800 |
JIS G3114 SMA570W Material Mechanical Properties
JIS G3114 SMA570W steel is known for its unique chemical and physical properties, which give it enhanced mechanical properties such as high tensile strength, yield strength, impact strength and hardness. Each grade has different properties and applications, so it is important to select the right grade for the specific application.
The mechanical properties of the JIS G3114 SMA570W steel are as follows:
| YieldRp0.2 | ≤ 267 (MPa) |
| TeileRm | ≤ 821 (MPa) |
| ImpactKV/Ku | 21(J) |
| ElongationA | 12% |
| Reduction in cross section on fractureZ | 32% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 311 |
JIS G3114 SMA570W Material Thermal Properties
The thermal performance parameters of the JIS G3114 SMA570W steel are as follows:
| Temperature (°C) | 11 | 446 | 466 |
| Modulus of elasticity (GPa) | - | 715 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 24 |
| Thermal conductivity (W/m·°C) | - | 43.3 | 44.2 |
| Specific thermal capacity (J/kg·°C) | - | 131 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.23 | - | - |
| Deity (kg/dm³) | - | - | 344 |
| Poisson’s coefficient, ν | - | - | 434 |
JIS G3114 SMA570W Material Machining Technology
Coolants are also important when machining JIS G3114 SMA570W steel as they can effectively reduce the heat generated by the cutting process and keep the cutting edge sharper for longer. Generally, a light emulsion or oil-based coolant should be used. Heavy concentrations of coolant should be avoided to prevent clogging in the cutting tool.