ASTM A582/A582M S44020 Introduce
Machining ASTM A582/A582M S44020 is a great way to create strong and durable parts. It is an alloy that has well-balanced properties, good machinability, and excellent strength and corrosion resistance. In order to achieve the best results, it is important to choose the right tooling, adjust the speeds and feeds accordingly, and consider chip formation. Cooling should also be used to prevent excessive wear and tear on the tooling. If issues arise while machining, troubleshooting steps can be taken to rectify the problem.
Smelting temperature:1459°C - 1772°C
Application:Standard Specification for High Speed cutting Stainless Steel Bars
ASTM A582/A582M S44020 Material Chemical Composition
The chemical composition of the ASTM A582/A582M S44020 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Silicon (Si) | - | 1.0000 |
| Sulfur (S) | 0.1500 | - |
| PhOsphorus (P) | - | 0.0600 |
| Nickel (Ni) | - | 0.5000 |
| Manganese (Mn) | - | 1.2500 |
| Copper (Cu) | - | 0.6000 |
| Chromium (Cr) | 16.0000 | 18.0000 |
| Carbon (C) | 0.9500 | 1.2000 |
ASTM A582/A582M S44020 Material Mechanical Properties
The mechanical properties of the ASTM A582/A582M S44020 steel are as follows:
| YieldRp0.2 | ≤ 465 (MPa) |
| TeileRm | ≤ 831 (MPa) |
| ImpactKV/Ku | 12(J) |
| ElongationA | 32% |
| Reduction in cross section on fractureZ | 43% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 334 |
ASTM A582/A582M S44020 Material Thermal Properties
The thermal performance parameters of the ASTM A582/A582M S44020 steel are as follows:
| Temperature (°C) | 33 | 896 | 119 |
| Modulus of elasticity (GPa) | - | 682 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 44 |
| Thermal conductivity (W/m·°C) | - | 21.3 | 22.2 |
| Specific thermal capacity (J/kg·°C) | - | 212 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.23 | - | - |
| Deity (kg/dm³) | - | - | 413 |
| Poisson’s coefficient, ν | - | - | 334 |