ASTM A409/A409M Type 310 Introduce
ASTM A409/A409M Type 310 is an alloy steel with a unique combination of mechanical and thermal properties. Its tensile strength, yield strength, and corrosion resistance make it a popular choice for demanding applications. Furthermore, the steel has excellent weldability, good formability, and can withstand high temperatures. It is also relatively easy to form and weld.
Smelting temperature:1178°C - 1228°C
Application:Corrosion resistant or high temperature resistant large diameter welded austenitic stainless steel tube
ASTM A409/A409M Type 310 Material Chemical Composition
The chemical composition of the ASTM A409/A409M Type 310 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Silicon (Si) | - | 1.5000 |
| Sulfur (S) | - | 0.0300 |
| PhOsphorus (P) | - | 0.0450 |
| Nickel (Ni) | 19.0000 | 22.0000 |
| Manganese (Mn) | - | 2.0000 |
| Chromium (Cr) | 24.0000 | 26.0000 |
| Carbon (C) | - | 0.2500 |
ASTM A409/A409M Type 310 Material Mechanical Properties
The mechanical properties of the ASTM A409/A409M Type 310 steel are as follows:
| YieldRp0.2 | ≤ 761 (MPa) |
| TeileRm | ≤ 744 (MPa) |
| ImpactKV/Ku | 21(J) |
| ElongationA | 31% |
| Reduction in cross section on fractureZ | 44% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 432 |
ASTM A409/A409M Type 310 Material Thermal Properties
The thermal performance parameters of the ASTM A409/A409M Type 310 steel are as follows:
| Temperature (°C) | 22 | 493 | 588 |
| Modulus of elasticity (GPa) | - | 592 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 43 |
| Thermal conductivity (W/m·°C) | - | 14.3 | 22.2 |
| Specific thermal capacity (J/kg·°C) | - | 221 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.32 | - | - |
| Deity (kg/dm³) | - | - | 122 |
| Poisson’s coefficient, ν | - | - | 333 |