DIN EN 10028-5 1.8828 Introduce
DIN EN 10028-5 is an European standard for hot-rolled flat products made of steels for pressure purposes. It applies to steels for pressure purposes with specified elevated temperature properties. These steel grades are also classified according to their chemical composition and mechanical properties. The mechanical properties of these steels are guaranteed by a range of tests specified in the standard. This type of steel is used in pressure vessels, boilers, steam lines, and steam turbines. The use of DIN EN 10028-5 1.8828 and its guidelines can help to increase safety and performance, while reducing the production costs associated with pressure equipment.
Smelting temperature:1887°C - 1159°C
Application:Pressure flat steel products - Part 5: Weldable fine grain steel, thermomechanical rolling
DIN EN 10028-5 1.8828 Material Chemical Composition
The chemical composition of the DIN EN 10028-5 1.8828 steel are as follows:
| Element | Min | Max |
|---|---|---|
| Vanadium (V) | - | 0.1000 |
| Titanium (Ti) | - | 0.0500 |
| Silicon (Si) | - | 0.5000 |
| Sulfur (S) | - | 0.0150 |
| PhOsphorus (P) | - | 0.0200 |
| Nickel (Ni) | - | 0.5000 |
| (Nb+Ti+V) | - | 0.1500 |
| Niobium (Nb) | - | 0.0500 |
| Nitrogen (N) | - | 0.0200 |
| Molybdenum (Mo) | - | 0.2000 |
| Manganese (Mn) | - | 1.7000 |
| (Cr+Cu+Mo) | - | 0.6000 |
| (CEV) | - | 0.4300 |
| Carbon (C) | - | 0.1600 |
| Aluminum (Al) | 0.0200 | - |
DIN EN 10028-5 1.8828 Material Mechanical Properties
The mechanical properties of the DIN EN 10028-5 1.8828 steel are as follows:
| YieldRp0.2 | ≤ 614 (MPa) |
| TeileRm | ≤ 553 (MPa) |
| ImpactKV/Ku | 42(J) |
| ElongationA | 33% |
| Reduction in cross section on fractureZ | 14% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 312 |
DIN EN 10028-5 1.8828 Material Thermal Properties
The thermal performance parameters of the DIN EN 10028-5 1.8828 steel are as follows:
| Temperature (°C) | 34 | 724 | 182 |
| Modulus of elasticity (GPa) | - | 616 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 22 |
| Thermal conductivity (W/m·°C) | - | 22.3 | 34.2 |
| Specific thermal capacity (J/kg·°C) | - | 444 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.42 | - | - |
| Deity (kg/dm³) | - | - | 231 |
| Poisson’s coefficient, ν | - | - | 431 |
DIN EN 10028-5 1.8828 Material Machining Technology
Steel is one of the most widely used materials in the world. It can be found in an array of different projects ranging from bridges, cars, and aircrafts to everyday home appliances and equipment. One of the most widely used steel grades is DIN EN 10028-5 1.8828, a high-strength, heat-treatable steel grade developed by the German Institute for Standardization (DIN). The availability of this type of steel has made it a popular choice in many applications. But due to its complex and unique characteristics, the machining of DIN EN 10028-5 1.8828 steel poses some noteworthy challenges.