GB/T 714 Q235qC Introduce
GB/T 714 Q235qC Steel is a metal alloy composed primarily of iron, carbon, and other elements such as manganese, phosphorus, sulfur, and silicon. Steel has a broad range of applications, from construction to machine parts, due to its strength, durability, and ability to be formed into various shapes and sizes.
Smelting temperature:1422°C - 1969°C
Application:Structural steel for bridge
GB/T 714 Q235qC Material Chemical Composition
The chemical composition of the GB/T 714 Q235qC steel are as follows:
| Element | Min | Max |
|---|---|---|
| Carbon (C) | - | 0.2000 |
| Silicon (Si) | - | 0.3000 |
| Manganese (Mn) | 0.4000 | 0.7000 |
| Sulfur (S) | - | 0.0350 |
| PhOsphorus (P) | - | 0.0350 |
| Silicon (Si) | - | 0.3500 |
| Sulfur (S) | - | 0.0300 |
| PhOsphorus (P) | - | 0.0300 |
| Nickel (Ni) | - | 0.3000 |
| Nitrogen (N) | - | 0.0120 |
| Manganese (Mn) | - | 1.4000 |
| Copper (Cu) | - | 0.3000 |
| Chromium (Cr) | - | 0.3000 |
| Carbon (C) | - | 0.1700 |
| Aluminum (Al) | 0.0150 | - |
GB/T 714 Q235qC Material Mechanical Properties
The mechanical properties of the GB/T 714 Q235qC steel are as follows:
| YieldRp0.2 | ≤ 144 (MPa) |
| TeileRm | ≤ 367 (MPa) |
| ImpactKV/Ku | 31(J) |
| ElongationA | 22% |
| Reduction in cross section on fractureZ | 21% |
| As-Heat-Treated Condition | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Brinell hardness (HBW) | 343 |
GB/T 714 Q235qC Material Thermal Properties
The thermal performance parameters of the GB/T 714 Q235qC steel are as follows:
| Temperature (°C) | 33 | 813 | 278 |
| Modulus of elasticity (GPa) | - | 479 | - |
| Mean coefficient of thermal expaion ×10-6/(°C) | - | - | 13 |
| Thermal conductivity (W/m·°C) | - | 23.3 | 13.2 |
| Specific thermal capacity (J/kg·°C) | - | 342 | - |
| Specific electrical resistivity (Ω mm²/m) | 0.14 | - | - |
| Deity (kg/dm³) | - | - | 442 |
| Poisson’s coefficient, ν | - | - | 241 |